Engineered Coated Fabrics |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
| STYLE# |
2257 |
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| DESCRIPTION / CONSTRUCTION |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 2 PLY D/C NEOPRENE/NYLON BIASED
YELLOW CURED |
|
|
|
|
|
|
|
|
|
|
|
|
|
| AREAS OF APPLICATIONS |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| FAA & TSO APPROVED RAFT AND
SLIDE FABRIC |
|
|
|
|
|
|
|
|
|
|
|
|
|
| CHARACTERITICS / PHYSICAL PROPERTIES |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| TEST / METHOD |
|
|
|
Federal Standard 191A or ASTM |
|
|
REQUIREMENT |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| FINISHED WIDTH |
|
|
|
|
|
|
50 INCHES (MIN USABLE) |
|
| FINISHED WEIGHT |
|
METHOD ASTM D751 |
8.5 OZ/SQ YD |
|
|
| BREAKING STRENGTH |
|
METHOD ASTM D751 |
WARP 190 LBS MIN FILL
190 LBS MIN |
|
| TEAR STRENGTH |
|
|
|
METHOD ASTM D751 |
WARP 13.0 LBS MIN FILL
13.0 LBS MIN |
|
| COATING ADHESION |
|
METHOD ASTM D751 |
5.0 LBS/INCH MIN |
|
|
| PLY ADHESION |
|
|
|
FED STD 191A METHOD
5960 |
5.0 LBS/INCH MIN |
|
|
| AIR RETENTION 5 MINUTES AT 10 PSI |
MIL-C-19002 |
|
NO LEAKS |
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| The
information contained herein was developed in our laboratories and is
believed reliable. It is offered in good faith. However, |
|
| as prospective users conditions
and methods of use are beyond our control, we recommend the user determine
the suitability |
|
| of this product before adapting
our materials on a commercial scale. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|